What is the yield strength of aluminum 6061 O?
What is the yield strength of aluminum 6061 O?
What is the yield strength of aluminum 6061 O?
6061-0. Annealed 6061 (6061-0 temper) has maximum tensile strength no more than 18,000 psi (125 MPa), and maximum yield strength no more than 8,000 psi (55 MPa).
What is the yield stress for aluminum?
Aluminum 6061-T6; 6061-T651
| Physical Properties | Metric | English |
|---|---|---|
| Ultimate Tensile Strength | 310 MPa | 45000 psi |
| Tensile Yield Strength | 276 MPa | 40000 psi |
| Elongation at Break | 12 % | 12 % |
| Elongation at Break | 17 % | 17 % |
What is the modulus of elasticity for 6061 aluminum?
68.9 GPa
Mechanical Properties
| Properties | Metric | Imperial |
|---|---|---|
| Fatigue strength | 96.5 MPa | 14000 psi |
| Elastic modulus | 68.9 GPa | 10000 ksi |
| Poisson’s ratio | 0.33 | 0.33 |
| Elongation | 12-17% | 12-17% |
What are the properties of aluminum 6061 T6?
Aluminum 6061 has good corrosion resistance, mechanical properties, formability, weldability, and machinability. Generally suitable for medium to high strength requirements, and has good toughness.
Which is better 6061 temper or T6 temper?
General 6061 characteristics and uses: Excellent joining characteristics, good acceptance of applied coatings. Combines relatively high strength, good workability, and high resistance to corrosion; widely available. The T8 and T9 tempers offer better chipping characteristics over the T6 temper.
What kind of corrosion resistance does Al 6061 have?
AL 6061 Alloy Corrosion Resistance AL 6061 alloy has excellent corrosion resistance to atmospheric conditions and good corrosion resistance to seawater. This alloy also has a good finish and a good reaction to anodic oxidation. However, where appearance is crucial, consider using 6063 alloy.
What is the compression modulus of aluminum 6061?
AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus. 2.5 cm width x 0.16 cm thick side-notched specimen, K t = 17. Estimated from trends in similar Al alloys.